Nylon 6.6 cord fabric (dipped)

1
2

Nylon 6.6 cord fabric (dipped)

Nylon 6.6 cord fabrics are used as a multilayer carcass in tires. Nylon 6.6 cord fabrics are used in aircraft tires and in “A” class passenger tires. They are characterized by high tenacity, steadiness to repeated bending strain, high moisture resistance and light load.

Fabric type Nylon-6.6 cord
fabric 11A
Nylon-6.6 cord
fabric 13ATLDU
Nylon-6.6 cord
fabric 132A
Nylon-6.6 cord
fabric 252A
Nylon-6.6 cord
fabric 30A
Nylon-6.6 cord
fabric 302A
Yarn structure 1400 dtex × 1 940 dtex × 1 × 2 940 dtex × 1 × 2 1880 dtex × 1 × 2 2100 dtex × 1 × 2 2100 dtex × 1 × 2
Thickness, mm 0,39±0,03 0,53±0,05 0,53±0,05 0,77±0,05 0,80±0,05 0,80±0,05
Breaking strength, N (kgs), not less 105 (11,0) 132,0 132,0 250,0 294,0 294,0
Elongation at 20 N, % 4,7±0,5 4,0±1,0 4,0±1,0 2,5±1,0 2,5±1,0 2,5±1,0
Elongation at 39 N, % 7,5±1,0 7,0±1,0 7,0±1,0 5,5±1,0 5,5±1,0 5,5±1,0
Elongation at break, % 17±2,0 16,0 16,0 20,0 21,0 21,0
Elongation at break, % 17±2,0 16,0 16,0 20,0 21,0 21,0
Linear shrinkage, %, not more 4,5 4,8 4,8 4,6 4,6 4,6
Heat resistance, %, not less 90,0 90,0 90,0 90,0 90,0 90,0
Twist 1 470±20 470±20 320±20 320±20 320±20
2 470±20 470±20 320±20 320±20 320±20
Fabric surface density, g/m2 160±20 268±20 195±20 305±20 445±20 355±20
H-test 10mm, N, not less 60 125 125 147 147 147
Mass fraction of an impregnation compound (weight gain)-DPU,% 4,5±2,0 4,5±2,0 4,5±2,0 4,5±2,0 4,5±2,0 4,5±2,0
Fabric width, cm In accordance with the customer’s requirements
The length of cord fabric in the roll, cm In accordance with the customer’s requirements

Note: all the properties could be changed in accordance with customers’ demands and specifications.

2018-2019 JSC TEXXCORE
63 Alexandrova St., Volzhsky, Volgograd region, 404103, Russian Federation
Location map
The content and design of the website includes materials from
www.gazprom.com and www.gazpromss.com